Glass fiber fabric for marine is bidirectional fabric made by interweaving direct rovings. fiberglass fabric are compatible with unsaturated polyester, vinyl ester, epoxy and phenolic resins.they are a high-performance reinforcement widely used in hand lay up and robot processes锛宭ight weight cloths of fiberglass fabric tend to provide a smooth finish and are excellent for producing a waterproofing layer over wood or other surfaces when combined with the appropriate resin. Heavier cloths of fiberglass fabric will provide greater strength and overall rigidity.
The roll width ranges from 50mm to 3000mm. Area Weight (g/m2):200 ~ 1600,special requirements is also available upon your need
Glass fiber composites deliver: design freedom, excellent corrosion resistance, reduced weight, as well as ease of maintenance. These benefits have made Fiberglass the dominant material for boat hulls and decks used on marine vessels from kayaks and canoes to power boats and luxurious yachts.
Product features
Electrical insulation resistance,excellent corrosion resistance
Low weight,flexible manufacturing
Difficult deformation,easy for operation
Fast and complete resin wet-out ,improve productivity
Excellent compatibility with resin,excellent mechanical property,
ModelYarnNominal linear density,TexSize code of yarnDensity (piece/10cm)Yarn consumptionCentral value of area weight
EWR400warp6003863250%400卤5
EWR400weft6003863250%400卤5
EWR600warp12003862652%600卤5
EWR600weft12003862448%600卤5
EWR800warp24003861854.5%792卤5
EWR800weft24003861545.85%792卤5
Inspection itemInspection methodEWR400E-100EWR600E-100EWR800E-100
Area weightGB/T 9914.3-2013365-403570-630758-832
Moisture contentGB/T 9914.1-20130.150.150.15
Warp breaking strengthGB/T 7689.5-2013鈮?400鈮?900鈮?400
Weft breaking strengthGB/T 7689.5-2013鈮?400鈮?600鈮?800
Warp yarn density(piece/10cm)GB/T 7689.5-20133.0-3.42.4-2.81.6-2.0
Weft yarn density(piece/10cm)GB/T 7689.5-20133.0-3.42.4-2.81.3-1.7
Storage
Unless otherwise specified, fiberglass products should be stored in a dry, cool and rain-proof area. The room temperature and humidity should be always maintained at 15 degree to 35 degree and 35%~65% respectively..
Our advantages
our company is the top one FRP distributor in south China has specialized in composites industry for over 16 years, with perfect quality and service , our professional ability gained high praise from our clients.
Payment &Shipping &Packing
We accept T/T,L/C,or Western Union , if you have any problems about payment,please feel free to contact us
Delivery time is around one week if we have stock , if without stock ,it will ship in 10-15 days after receiving the deposit
Woven Rovings are wound onto a paper tube which has an inside diameter of 89mm, and the roll has a diameter of 260mm. The roll is wrapped up with plastic film, and then packed in a cardboard box or wrapped up with kraft paper. The rolls are to be horizontally placed. For transportation the rolls can be loaded into a container directly or on pallet
Tips of hand lay-up process
Hand Lay-up is an open molding process. The reinforcement, in form of fiberglass strands, mat, or woven roving, is first laid into a mold which has been coated with a release agent and a gel coat. Then a resin mix is applied by hand, using a brush or spray gun. A roller is then used to ensure uniform impregnation, complete wet-out and removal of any trapped air bubbles.Customized Glass Fiber Fabric
website:http://www.bohaocomposites.com/fiberglass-fabric/glass-fiber-fabric/